Supply Nickel Alloy Coil by Grade N06601/6023

Model NO.: N06601/6023 Standard: AISI, ASTM, DIN, JIS, GB, BS Composition: Stainless Steel Scrap Shape: Plate Special Use: Wear Resistant Steel Size: as Your Requirment Specification: SGS, CE, RoSH Type: Coil Steel Grade: Nickel Alloy Coil Technique: Cold Rolled Surface Treatment: 2b,2e Application: Chemical Processing Pollution Pulp Paper Indust Port: Shanghai, Ningbo Origin: Mainland China Quick Details

Place of Origin: China (Mainland)
Type: Nickel Strip
Application: Chemical processing Pollution control Pulp and paper production Indust
Grade: Nickel Alloy N06601/6023 coil
Ni (Min): up to standard
Resistance (μΩ.m): up to standard
Powder Or Not: Not Powder
Ultimate Strength (≥ MPa): up to standard
Elongation (≥ %): up to standard
Model Number: Nickel Alloy N06601/6023 coil
Brand Name: FLS
surface: 2B,2E
name: Supply Nickel Alloy N06601/6023 coil
our services: after-services
note: we also provide other meterials
size: as your requirment
delivery: short
small order: do best
sample: free


Packaging & Delivery
Packaging Details:Delivery Detail:

standard seaworthy export packing or based on customer's requirement.  For:Supply Nickel Alloy N06601/6023 coil

7-15 days after received your deposit.

 
Supply Nickel Alloy N06601/6023 coil
Introduction
Nicrofer 6023 alloy is a nickel-chromium-iron alloy with excellent resistance to corrosion and oxidation at elevated temperatures. The alloy is precipitation-hardenable, and exhibits good mechanical properties at high temperatures.
The following datasheet will provide an overview of nicrofer 6023 alloy.
Chemical Composition
The chemical composition of nicrofer 6023 alloy is outlined in the following table.


ElementContent (%)

Nickel, Ni	58-63
Chromium, Cr	21-25
Aluminum, Al	1-1.7
Copper, Cu	1
Manganese, Mn	1
Silicon, Si	0.5
Carbon, C	0.1
Sulfur, S	0.015
Iron, Fe	Balance

Physical Properties
The following table shows the physical properties of nicrofer 6023 alloy.
PropertiesMetricImperial

Density	8.11 g/cm3	0.293 lb/in3
Melting point	1360-1411°C	2480-2572°F

Mechanical Properties
The mechanical properties of nicrofer 6023 alloy are displayed in the following table.
PropertiesMetricImperial

Tensile strength (Solution annealed)	760 MPa	110000 psi
Yield strength (Solution annealed)	450 MPa	65300 psi
Elongation at break (Solution annealed)	42%	42%

Thermal Properties
The thermal properties of nicrofer 6023 alloy are given in the following table.
PropertiesMetricImperial

Thermal expansion co-efficient (@20-100°C/68-212°F)	13.75 µm/m°C	7.639 µin/in°F
Thermal conductivity	11.2 W/mK	77.7 BTU.in/hrft².°F

Machinability
Conventional machining techniques that are used for machining iron-based alloys can be used.

Forming
Nicrofer 6023 alloy has excellent ductility, and can be readily formed by all conventional techniques.

Welding
The alloy can be welded using commonly used welding techniques such as gas-tungsten arc welding, shielded metal-arc welding, gas metal-arc welding and submerged-arc welding.

Forging
The alloy can be forged in the temperature range of 1038 to 1232°C (1900 to 2250°F).

Hot Working
Hot working of nicrofer 6023 alloy can be performed in the temperature range of 871 to 1232°C (1600 to 2250°F).

Cold working
Cold working may be performed using standard tooling.

Annealing
The alloy can be annealed at 1149°C (2100°F) and then rapidly cooled to avoid thermal cracking.
 

Contact us if you need more details on Nickel Alloy Coil. We are ready to answer your questions on packaging, logistics, certification or any other aspects about Nickel Coil、Steel Coil. If these products fail to match your need, please contact us and we would like to provide relevant information.

Product Categories : Nickel & Nickel Alloy