Nickel Alloy Bar Technique: Hot Rolled Surface Treatment: Polished Application: Aerospace,Chemical Industry,Oil Specification: SGS, CE, RoSH Quick Details Place of Origin: China (Mainland) Type: Nickel Bar Application: Chemical processing, Food processing Grade: Nickel Bar Ni (Min): up to standard Resistance (μΩ.m): up to standard Powder Or Not: Not Powder Ultimate Strength (≥ MPa): up to standard Elongation (≥ %): up to standard Model Number: inconel 600 bar Brand Name: FLS Name: inconel 600 bar Surface: polished Technique: Solution annealing,descaling Best service: after-sales services Note: we can do other material Sample: Can offer State: plate/tube/rod Stocks: 800 tons Delivery: Short Small order: Can do best Packaging & Delivery
Packaging Details: | Standard export packing or as your requirement for Nickel alloy bar/ inconel 600 bar/inconel 600 bar/inconel 600 |
Nickel alloy bar / inconel 600 bar / inconel 600 bar / inconel 600 Product Description Inconel® 600 is a nickel-base alloy with excellent carburization, and good oxidation resistance at elevated temperatures. The alloy has long been used in the heat treating industry for many of the same applications as RA330®. 600 alloy has useful resistance to dry Cl2 and HCl gases at moderately elevated temperatures. Alloy 600 is not suggested for use at red heat when sulfur is present due to elevated nickel quantities.
Grades 200 and 201 nickel are normally preferred for handling concentrated, high temperature caustic. However, when sulfur compounds are present as well, or for ammonium hydroxide service, 600 alloy is suggested. 600 alloy is subject to stress corrosion cracking in hot, concentrated caustic alkalies. To avoid stress corrosion cracking, the 600 alloy fabrication should be fully stress relieved prior to use. A minimum treatment of 1650°F for 1 hour is suggested, but 1800-1850°F for 1 hour preferred. Chemistry
| Ni | Cr | C | Mn | Cu | Si | S | Fe |
MIN | 72.00 | 14.00 | -- | -- | -- | -- | -- | 6.00 |
MAX | | 17.00 | 0.15 | 1.00 | 0.50 | 0.50 | 0.015 | 10.00 |
*ASTM specification 0.20 max C. Inventory 600 Plate, 600 Rod Coil, 600 Round Bar, 600 Sheet, 600 Welding Products Common Trade Names Alloy 600, Inconel® 600, Nickel 600 Applications Heat treating muffles and retorts Vacuum furnace fixtures Chlorination equipment to 1000°F Titanium dioxide plants Physical Properties Density: 0.304 lb/in3 Melting Point: 2470- 2575°F Poisson's Ratio: 0.29 Electrical Resistivity: 620 Ohm-circ mil/ft
Temperature, °F | 70 | 1000 | 1200 | 1400 | 1600 | 2000 |
Coefficient* of Thermal Expansion, in/in°F x 10-6 | - | 8.4 | 8.6 | 8.7 | 9.1 | 9.3 |
Thermal Conductivity Btu • ft/ft2 • hr • °F | 8.6 | 13.2 | 14.3 | 13.0 | 16.7 | - |
Modulus of Elasticity, Dynamic psi x 106 | 30.0 | 25.6 | 24.5 | 23.6 | 22.2 | 20.4 |
* 70°F to indicated temperature. Mechanical Properties Representative Tensile Properties
Temperature,°F | 70 | 1000 | 1200 | 1400 | 1600 | 1800 |
Ultimate Tensile Strength, ksi | 93 | 84 | 65 | 27.5 | 15 | 7.5 |
0.2% Yield Strength, ksi | 37 | 28.5 | 26.5 | 17 | 9.0 | 4.0 |
Charpy Impact V-notch, ft-lbs | 45 | 47 | 39 | 46 | 80 | 118 |
Static Corrosion in Molten Caustic Soda Corrosion Rate, Mils Per Year
Temperature, °F | 750 | 932 | 1076 | 1256 |
Alloy 201 | 0.9 | 1.3 | 2.5 | 37.8 |
Alloy 400 | 1.8 | 5.1 | 17.6 | - |
Alloy 600 | 1.1 | 2.4 | 5.1 | 66.4 |
Contact us if you need more details on Nickel Alloy Bar. We are ready to answer your questions on packaging, logistics, certification or any other aspects about Alloy Round Bar、Nickel Round Bar. If these products fail to match your need, please contact us and we would like to provide relevant information.