Best Price Nickel Alloy Bar by N07718

Model NO.: N07718 Standard: AISI, ASTM, DIN, JIS, GB, BS Composition: Stainless Steel Scrap Shape: Round Bar Special Use: High-strength Steel Plate Port: Shanghai, Ningbo Origin: Mainland China Type: Alloy Steel Bar Steel Grade: Nickel Alloy Bar Technique: Hot Rolled Surface Treatment: Polished Application: Aerospace, Chemical Industry, Oil Specification: SGS, CE, RoSH Quick Details Place of Origin: China (Mainland) Type: Nickel Bar     Grade: bar Ni (Min): 50 Resistance (μΩ.m): up to standard Powder Or Not: Not Powder Ultimate Strength (≥ MPa): up to standard Elongation (≥ %): up to standard Model Number: Inconel 718 Brand Name: FLS Name: N07718/Inconel 718 Nickel and Nickel Alloy Bar & Rod Surface: polished Technique: Solution annealing,descaling Best service: after-sales services Note: we can do other material Mill testing: third party testing Packaging & Delivery

Packaging Details:	Standard export packing or as your requirement for China supplier N07718/Inconel 718 Nickel and Nickel Alloy Bar & Rod
Delivery Detail:	7-20days

  China supplier N07718/Inconel 718 Nickel and Nickel Alloy Bar & Rod   Product Description   Specification Inconel 718 is a Nickel-Chromium alloy being precipitation hardenable and having high creep-rupture strength at high temperatures to about 700°C (1290°F). It has higher strength thanInconel X-750 and better mechanical properties at lower temperatures than Nimonic 90 andInconel X-750.

Form	Specification
Bar & Rod	Rolled barΦ5-45mm,Length≤1500mm
	Forged barΦ26-245mm,Length≤4000mm
Standard	AMS 5663/ AMS 5832/ AMS 5962/ AMS 5662/ ASTM B637
Application

Chemical Composition 

Element	Content
Ni+Co	50 - 55 %
Cr	17 - 21 %
Fe	BAL
Nb+Ta	4.75 - 5.5 %
Mo	2.8 - 3.3 %
Ti	0.65 - 1.15 %
Al	0.2 - 0.8 %

Typical Properties

Property	Metric	Imperial
Density	8.19 g/cm3	0.296 lb/in3
Melting point	1336 °C	2437 °F
Co-Efficient of Expansion	13.0 µm/m.°C (20-100 °C)	7.2x10-6 in/in.°F (70-212 °F)
Modulus of rigidity	77.2 kN/mm2	11197 ksi
Modulus of elasticity	204.9 kN/mm2	29719 ksi

Properties of Supplied Materials and Heat Treated Materials

Condition of Supply	Heat Treatment (After Forming)
No.1 Spring Temper/Spring Temper	1. Solution Anneal at 980°C (1800°F) for 1 hour and air cool and 2. Age harden at 720°C (1330°F) for 8 hours and furnace cool to 620°C (1150°F) and hold at 620°C (1150°F) for a total age hardening time of 18 hours and air cool.
No.1 Spring Temper/Spring Temper (NACE MRO175)	1. 1010°C (1870°F) 2 hours and air cool and 2. 790°C (1455°F) 6 hours and air cool.
Condition	Approx Tensile Strength		Approx Service Temp.
Annealed	800 - 1000 N/mm2	116 - 145 ksi	-	-
No.1 Spring Temper	1000 - 1200 N/mm2	145 - 175 ksi	-	-
No.1 Spring Temper + Annealed + Aged	1250 - 1450 N/mm2	181 - 210 ksi	-200 to +550°C	-330 to +1020°F
Spring Temper	1300 - 1500 N/mm2	189 - 218 ksi	-	-
Spring Temper + Annealed + Aged	1250 - 1450 N/mm2	181 - 210 ksi	-200 to +550°C	-330 to +1020°F

Contact us if you need more details on Nickel Alloy Bar. We are ready to answer your questions on packaging, logistics, certification or any other aspects about Nickel Bar、Nickel Alloy Rod. If these products fail to match your need, please contact us and we would like to provide relevant information.

Product Categories : Nickel & Nickel Alloy